Surface integrity assessment of laser treated and subsequently coated cemented carbides

Shiqi Fang, Fernando García Marro, Nuria Salan, Marlon Cruz, Carles Colominas, Dirk Bähre, Luis Llanes

Producción científica: Artículo en revista indizadaArtículorevisión exhaustiva

9 Citas (Scopus)

Resumen

Cemented carbides, referred to as hardmetals, are forefront engineering materials widely implemented in industry for chip-removal cutting tools and supporting parts. As a newly developed technology for surface modification with high precision, the application of short pulse laser may extend the utilization of cemented carbides. However, surface integrity of laser-treated materials may be affected during the ablation phenomena. These potential changes may also be relevant for subsequent coating deposition, a surface modification stage usually invoked in many cutting and forming tools. It is the objective of this work to study the influence of a previous laser treatment on the surface integrity of a cemented carbide grade, finally coated by a ceramic layer introduced by physical vapor deposition. In doing so, a nanosecond laser has been employed. Surface integrity is assessed in terms of roughness, hardness, and microstructural changes induced at the subsurface level. It is found that pulse laser can effectively remove the target material, resulting roughness being similar to that attained by abrasive grinding. Although some subsurface damage is observed, it is limited to a very shallow layer, this being thoroughly eliminated during sandblasting implemented before coating deposition. Relative hardness increase is larger for laser treated substrate than for just polished one, reason behind it being speculated to come from the sandblasting stage used for removing damaged layer.

Idioma originalInglés
Número de artículo104982
PublicaciónInternational Journal of Refractory Metals and Hard Materials
Volumen83
DOI
EstadoPublicada - sept 2019
Publicado de forma externa

Huella

Profundice en los temas de investigación de 'Surface integrity assessment of laser treated and subsequently coated cemented carbides'. En conjunto forman una huella única.

Citar esto