Oxide scale formation on 316L and FeCrAl steels exposed to oxygen controlled static LBE at temperatures up to 800 °C

C. Cionea, M. D. Abad, Y. Aussat, D. Frazer, A. J. Gubser, P. Hosemann

Producción científica: Artículo en revista indizadaArtículorevisión exhaustiva

69 Citas (Scopus)

Resumen

The corrosion behavior of three stainless steels (316L, Alkrothal 720 and Kanthal-APM) in static LBE with oxygen concentration of 10-5 wt% at temperatures of 700 °C for 230 h and 800 °C for 360 h was studied. The steel surface morphology of the oxide scales formed was investigated by SEM, XRD and Raman spectroscopy and the cross-section by SEM and EDX. A transitional inner-layer of Fe-Cr-Al oxides was found at the substrate interface and an Al-oxide outer layer on the Fe-Cr-Al alloys. Fast growing non-protective oxide scale with underlying dissolution was observed on the 316L alloy.

Idioma originalInglés
Páginas (desde-hasta)235-246
Número de páginas12
PublicaciónSolar Energy Materials and Solar Cells
Volumen144
DOI
EstadoPublicada - 1 ene 2016
Publicado de forma externa

Huella

Profundice en los temas de investigación de 'Oxide scale formation on 316L and FeCrAl steels exposed to oxygen controlled static LBE at temperatures up to 800 °C'. En conjunto forman una huella única.

Citar esto